Solder Alloy 716 vs. EN 1.4419 Stainless Steel

Solder alloy 716 belongs to the otherwise unclassified metals classification, while EN 1.4419 stainless steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is solder alloy 716 and the bottom bar is EN 1.4419 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
200
Elongation at Break, % 13
11 to 17
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 19
76
Tensile Strength: Ultimate (UTS), MPa 39
660 to 1590

Thermal Properties

Latent Heat of Fusion, J/g 60
280
Melting Completion (Liquidus), °C 230
1440
Melting Onset (Solidus), °C 220
1400
Specific Heat Capacity, J/kg-K 220
480
Thermal Conductivity, W/m-K 60
30
Thermal Expansion, µm/m-K 22
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 16
3.2

Otherwise Unclassified Properties

Density, g/cm3 7.3
7.7
Embodied Carbon, kg CO2/kg material 16
2.2
Embodied Energy, MJ/kg 270
30

Common Calculations

Stiffness to Weight: Axial, points 3.8
14
Stiffness to Weight: Bending, points 17
25
Strength to Weight: Axial, points 1.5
24 to 57
Strength to Weight: Bending, points 3.5
22 to 39
Thermal Diffusivity, mm2/s 37
8.1
Thermal Shock Resistance, points 2.5
23 to 55

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0.36 to 0.42
Chromium (Cr), % 0
13 to 14.5
Copper (Cu), % 0.3 to 0.7
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
82 to 86
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0.6 to 1.0
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0.8 to 1.2
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 97.6 to 98.9
0
Zinc (Zn), % 0 to 0.0010
0