MakeItFrom.com
Menu (ESC)

Solder Alloy 716 vs. EN 2.4608 Nickel

Solder alloy 716 belongs to the otherwise unclassified metals classification, while EN 2.4608 nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is solder alloy 716 and the bottom bar is EN 2.4608 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
210
Elongation at Break, % 13
34
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 19
81
Tensile Strength: Ultimate (UTS), MPa 39
620

Thermal Properties

Latent Heat of Fusion, J/g 60
330
Melting Completion (Liquidus), °C 230
1460
Melting Onset (Solidus), °C 220
1410
Specific Heat Capacity, J/kg-K 220
460
Thermal Conductivity, W/m-K 60
11
Thermal Expansion, µm/m-K 22
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 16
1.6

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.5
Embodied Carbon, kg CO2/kg material 16
8.4
Embodied Energy, MJ/kg 270
120

Common Calculations

Stiffness to Weight: Axial, points 3.8
14
Stiffness to Weight: Bending, points 17
23
Strength to Weight: Axial, points 1.5
20
Strength to Weight: Bending, points 3.5
19
Thermal Diffusivity, mm2/s 37
2.9
Thermal Shock Resistance, points 2.5
16

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0.030 to 0.080
Chromium (Cr), % 0
24 to 26
Cobalt (Co), % 0
2.5 to 4.0
Copper (Cu), % 0.3 to 0.7
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
11.4 to 23.8
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 4.0
Nickel (Ni), % 0 to 0.010
44 to 47
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.7 to 1.5
Silver (Ag), % 0.8 to 1.2
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 97.6 to 98.9
0
Tungsten (W), % 0
2.5 to 4.0
Zinc (Zn), % 0 to 0.0010
0