Solder Alloy 716 vs. Grade C-2 Titanium

Solder alloy 716 belongs to the otherwise unclassified metals classification, while grade C-2 titanium belongs to the titanium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is solder alloy 716 and the bottom bar is grade C-2 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 13
180
Elastic (Young's, Tensile) Modulus, GPa 51
110
Elongation at Break, % 13
17
Poisson's Ratio 0.36
0.32
Shear Modulus, GPa 19
40
Tensile Strength: Ultimate (UTS), MPa 39
390

Thermal Properties

Latent Heat of Fusion, J/g 60
420
Melting Completion (Liquidus), °C 230
1660
Melting Onset (Solidus), °C 220
1610
Specific Heat Capacity, J/kg-K 220
540
Thermal Conductivity, W/m-K 60
21
Thermal Expansion, µm/m-K 22
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 16
7.1

Otherwise Unclassified Properties

Density, g/cm3 7.3
4.5
Embodied Carbon, kg CO2/kg material 16
31
Embodied Energy, MJ/kg 270
510

Common Calculations

Stiffness to Weight: Axial, points 3.8
13
Stiffness to Weight: Bending, points 17
35
Strength to Weight: Axial, points 1.5
24
Strength to Weight: Bending, points 3.5
26
Thermal Diffusivity, mm2/s 37
8.8
Thermal Shock Resistance, points 2.5
30

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 0.3 to 0.7
0
Gold (Au), % 0 to 0.050
0
Hydrogen (H), % 0
0 to 0.015
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0 to 0.2
Lead (Pb), % 0 to 0.070
0
Nickel (Ni), % 0 to 0.010
0 to 0.050
Oxygen (O), % 0
0 to 0.4
Silver (Ag), % 0.8 to 1.2
0
Tin (Sn), % 97.6 to 98.9
0
Titanium (Ti), % 0
98.8 to 100
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.4