Solder Alloy 716 vs. N06255 Nickel

Solder alloy 716 belongs to the otherwise unclassified metals classification, while N06255 nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is solder alloy 716 and the bottom bar is N06255 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 51
210
Elongation at Break, % 13
45
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 19
81
Tensile Strength: Ultimate (UTS), MPa 39
660

Thermal Properties

Latent Heat of Fusion, J/g 60
320
Melting Completion (Liquidus), °C 230
1470
Melting Onset (Solidus), °C 220
1420
Specific Heat Capacity, J/kg-K 220
450
Thermal Expansion, µm/m-K 22
13

Otherwise Unclassified Properties

Density, g/cm3 7.3
8.5
Embodied Carbon, kg CO2/kg material 16
9.4
Embodied Energy, MJ/kg 270
130

Common Calculations

Stiffness to Weight: Axial, points 3.8
14
Stiffness to Weight: Bending, points 17
23
Strength to Weight: Axial, points 1.5
22
Strength to Weight: Bending, points 3.5
20
Thermal Shock Resistance, points 2.5
17

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
23 to 26
Copper (Cu), % 0.3 to 0.7
0 to 1.2
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
6.0 to 24
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
6.0 to 9.0
Nickel (Ni), % 0 to 0.010
47 to 52
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0.8 to 1.2
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 97.6 to 98.9
0
Titanium (Ti), % 0
0 to 0.69
Tungsten (W), % 0
0 to 3.0
Zinc (Zn), % 0 to 0.0010
0