ISO-WD32250 Magnesium vs. 90-silver 10-tin-oxide
ISO-WD32250 magnesium belongs to the magnesium alloys classification, while 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is ISO-WD32250 magnesium and the bottom bar is 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 77 to 82 |
| Elongation at Break, % | 4.5 to 8.6 | |
| 7.0 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 26 | |
| 20 to 68 |
| Shear Strength, MPa | 180 to 190 | |
| 160 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 330 | |
| 230 to 300 |
| Tensile Strength: Yield (Proof), MPa | 240 to 290 | |
| 120 to 280 |