ISO-WD32250 Magnesium vs. ASTM Grade LC3 Steel

ISO-WD32250 magnesium belongs to the magnesium alloys classification, while ASTM grade LC3 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ISO-WD32250 magnesium and the bottom bar is ASTM grade LC3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 4.5 to 8.6
27
Fatigue Strength, MPa 170 to 210
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Tensile Strength: Ultimate (UTS), MPa 310 to 330
570
Tensile Strength: Yield (Proof), MPa 240 to 290
310

Thermal Properties

Latent Heat of Fusion, J/g 340
250
Maximum Temperature: Mechanical, °C 120
410
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 550
1420
Specific Heat Capacity, J/kg-K 980
470
Thermal Conductivity, W/m-K 130
52
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 25
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 130
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
4.0
Density, g/cm3 1.8
7.9
Embodied Carbon, kg CO2/kg material 24
1.7
Embodied Energy, MJ/kg 160
23
Embodied Water, L/kg 950
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 14 to 26
130
Resilience: Unit (Modulus of Resilience), kJ/m3 630 to 930
260
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 67
24
Strength to Weight: Axial, points 49 to 51
20
Strength to Weight: Bending, points 58 to 60
19
Thermal Diffusivity, mm2/s 72
14
Thermal Shock Resistance, points 19 to 20
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.15
Iron (Fe), % 0
94.4 to 96.5
Magnesium (Mg), % 94.9 to 97.1
0
Manganese (Mn), % 0
0.5 to 0.8
Nickel (Ni), % 0
3.0 to 4.0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0
0 to 0.045
Zinc (Zn), % 2.5 to 4.0
0
Zirconium (Zr), % 0.45 to 0.8
0
Residuals, % 0 to 0.3
0