ISO-WD32260 Magnesium vs. N06230 Nickel
ISO-WD32260 magnesium belongs to the magnesium alloys classification, while N06230 nickel belongs to the nickel alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ISO-WD32260 magnesium and the bottom bar is N06230 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 210 |
| Elongation at Break, % | 4.5 to 6.0 | |
| 38 to 48 |
| Fatigue Strength, MPa | 150 to 190 | |
| 250 to 360 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 18 | |
| 83 |
| Shear Strength, MPa | 190 to 200 | |
| 420 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 340 | |
| 620 to 840 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 330 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 990 |
| Melting Completion (Liquidus), °C | 600 | |
| 1370 |
| Melting Onset (Solidus), °C | 520 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 420 |
| Thermal Conductivity, W/m-K | 110 | |
| 8.9 |
| Thermal Expansion, µm/m-K | 27 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 1.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 85 |
| Density, g/cm3 | 1.9 | |
| 9.5 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 11 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 940 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 19 | |
| 200 to 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 to 700 | |
| 250 to 380 |
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 63 | |
| 21 |
| Strength to Weight: Axial, points | 48 to 51 | |
| 18 to 25 |
| Strength to Weight: Bending, points | 56 to 58 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 63 | |
| 2.3 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 17 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.2 to 0.5 |
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 20 to 24 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Iron (Fe), % | 0 | |
| 0 to 3.0 |
| Lanthanum (La), % | 0 | |
| 0.0050 to 0.050 |
| Magnesium (Mg), % | 92.7 to 94.8 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 3.0 |
| Nickel (Ni), % | 0 | |
| 47.5 to 65.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.25 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 13 to 15 |
| Zinc (Zn), % | 4.8 to 6.2 | |
| 0 |
| Zirconium (Zr), % | 0.45 to 0.8 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |