ISO-WD43150 Magnesium vs. AWS BAg-10

ISO-WD43150 magnesium belongs to the magnesium alloys classification, while AWS BAg-10 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ISO-WD43150 magnesium and the bottom bar is AWS BAg-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
82
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 18
30
Tensile Strength: Ultimate (UTS), MPa 250
140

Thermal Properties

Latent Heat of Fusion, J/g 350
130
Melting Completion (Liquidus), °C 610
740
Melting Onset (Solidus), °C 590
690
Specific Heat Capacity, J/kg-K 990
280
Thermal Expansion, µm/m-K 27
20

Otherwise Unclassified Properties

Density, g/cm3 1.7
9.8

Common Calculations

Stiffness to Weight: Axial, points 15
4.6
Stiffness to Weight: Bending, points 71
15
Strength to Weight: Axial, points 41
4.0
Strength to Weight: Bending, points 52
6.1
Thermal Shock Resistance, points 14
6.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 0 to 0.050
19 to 21
Magnesium (Mg), % 97.5 to 98.8
0
Manganese (Mn), % 1.2 to 2.0
0
Nickel (Ni), % 0 to 0.010
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
69 to 71
Zinc (Zn), % 0
8.0 to 12
Residuals, % 0 to 0.3
0 to 0.15