K1A Magnesium vs. SAE-AISI 4620 Steel

K1A magnesium belongs to the magnesium alloys classification, while SAE-AISI 4620 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is K1A magnesium and the bottom bar is SAE-AISI 4620 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 43
190
Elongation at Break, % 13
16 to 27
Fatigue Strength, MPa 39
260 to 360
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 55
320 to 420
Tensile Strength: Ultimate (UTS), MPa 180
490 to 680
Tensile Strength: Yield (Proof), MPa 51
350 to 550

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 120
410
Melting Completion (Liquidus), °C 650
1460
Melting Onset (Solidus), °C 650
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 120
47
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 170
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
3.2
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 24
1.6
Embodied Energy, MJ/kg 170
22
Embodied Water, L/kg 970
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
100 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 30
330 to 800
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 73
24
Strength to Weight: Axial, points 31
17 to 24
Strength to Weight: Bending, points 43
18 to 22
Thermal Diffusivity, mm2/s 75
13
Thermal Shock Resistance, points 11
15 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.17 to 0.22
Iron (Fe), % 0
96.4 to 97.4
Magnesium (Mg), % 98.7 to 99.6
0
Manganese (Mn), % 0
0.45 to 0.65
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0
1.7 to 2.0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.3
0