K1A magnesium belongs to the magnesium alloys classification, while C72800 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is K1A magnesium and the bottom bar is C72800 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 43
120
Elongation at Break, % 13
3.9 to 23
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
44
Shear Strength, MPa 55
330 to 740
Tensile Strength: Ultimate (UTS), MPa 180
520 to 1270
Tensile Strength: Yield (Proof), MPa 51
250 to 1210

Thermal Properties

Latent Heat of Fusion, J/g 350
210
Maximum Temperature: Mechanical, °C 120
200
Melting Completion (Liquidus), °C 650
1080
Melting Onset (Solidus), °C 650
920
Specific Heat Capacity, J/kg-K 1000
380
Thermal Conductivity, W/m-K 120
55
Thermal Expansion, µm/m-K 27
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30
11
Electrical Conductivity: Equal Weight (Specific), % IACS 170
11

Otherwise Unclassified Properties

Base Metal Price, % relative 13
38
Density, g/cm3 1.6
8.8
Embodied Carbon, kg CO2/kg material 24
4.4
Embodied Energy, MJ/kg 170
68
Embodied Water, L/kg 970
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
37 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 30
260 to 5650
Stiffness to Weight: Axial, points 15
7.4
Stiffness to Weight: Bending, points 73
19
Strength to Weight: Axial, points 31
17 to 40
Strength to Weight: Bending, points 43
16 to 30
Thermal Diffusivity, mm2/s 75
17
Thermal Shock Resistance, points 11
19 to 45

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.1
Antimony (Sb), % 0
0 to 0.020
Bismuth (Bi), % 0
0 to 0.0010
Boron (B), % 0
0 to 0.0010
Copper (Cu), % 0
78.3 to 82.8
Iron (Fe), % 0
0 to 0.5
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 98.7 to 99.6
0.0050 to 0.15
Manganese (Mn), % 0
0.050 to 0.3
Nickel (Ni), % 0
9.5 to 10.5
Niobium (Nb), % 0
0.1 to 0.3
Phosphorus (P), % 0
0 to 0.0050
Silicon (Si), % 0
0 to 0.050
Sulfur (S), % 0
0 to 0.0025
Tin (Sn), % 0
7.5 to 8.5
Titanium (Ti), % 0
0 to 0.010
Zinc (Zn), % 0
0 to 1.0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0 to 0.3
0 to 0.3