Lead-alkali-silica Glass vs. Aluminum Titanate
Lead-alkali-silica glass belongs to the glass and glass-ceramics classification, while aluminum titanate belongs to the oxide-based engineering ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is lead-alkali-silica glass and the bottom bar is aluminum titanate.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.1 | |
| 3.2 |
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 13 |
| Flexural Strength, MPa | 34 | |
| 29 |
| Stiffness to Weight: Axial, points | 12 | |
| 2.2 |
| Stiffness to Weight: Bending, points | 43 | |
| 24 |
| Thermal Expansion, µm/m-K | 9.0 | |
| 2.9 |