Lead-alkali-silica Glass vs. Boron Carbide

Lead-alkali-silica glass belongs to the glass and glass-ceramics classification, while boron carbide belongs to the non-oxide engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is lead-alkali-silica glass and the bottom bar is boron carbide.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 3.1
2.1 to 2.7
Elastic (Young's, Tensile) Modulus, GPa 67
240 to 460
Electrical Resistivity Order of Magnitude, 10x Ω-m 12
0 to 11
Flexural Strength, MPa 34
170 to 410
Stiffness to Weight: Axial, points 12
63 to 100
Stiffness to Weight: Bending, points 43
91 to 100
Thermal Expansion, µm/m-K 9.0
4.5 to 5.6