LCP vs. PS
Both LCP and PS are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is LCP and the bottom bar is PS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 11 to 24 | |
| 1.9 to 2.9 |
| Elongation at Break, % | 1.0 to 3.0 | |
| 1.8 to 40 |
| Flexural Strength, MPa | 160 to 320 | |
| 62 to 80 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 230 | |
| 32 to 44 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 520 | |
| 320 to 330 |
| Specific Heat Capacity, J/kg-K | 1020 to 1200 | |
| 1250 to 1400 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.0 |
| Limiting Oxygen Index (LOI), % | 35 | |
| 18 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.4 to 8.9 | |
| 1.0 to 1.5 |
| Stiffness to Weight: Bending, points | 51 to 65 | |
| 40 to 45 |
| Strength to Weight: Axial, points | 33 to 43 | |
| 8.5 to 12 |
| Strength to Weight: Bending, points | 45 to 56 | |
| 22 to 26 |