Lithium Fluoride vs. Borosilicate Glass
Lithium fluoride belongs to the non-glass optical ceramics classification, while borosilicate glass belongs to the glass and glass-ceramics. There are 14 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is lithium fluoride and the bottom bar is borosilicate glass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 67 to 80 |
| Poisson's Ratio | 0.27 | |
| 0.21 |
Thermal Properties
| Melting Onset (Solidus), °C | 870 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 1560 | |
| 830 |
| Thermal Conductivity, W/m-K | 12 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 32 | |
| 3.3 to 5.1 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 9.0 | |
| 5.4 |
| Electrical Dissipation At 1 MHz | 0.00020 | |
| 0.0017 to 0.0088 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.6 | |
| 2.2 to 2.6 |
| Light Transmission Range, µm | 0.12 to 6.5 | |
| 0.3 to 2.5 |
| Refractive Index | 1.4 | |
| 1.5 |
Common Calculations
| Stiffness to Weight: Axial, points | 24 | |
| 15 to 17 |
| Stiffness to Weight: Bending, points | 62 | |
| 55 to 61 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 0.54 to 0.63 |