R31537 Cobalt vs. Chromium 33

R31537 cobalt belongs to the cobalt alloys classification, while chromium 33 belongs to the otherwise unclassified metals. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R31537 cobalt and the bottom bar is chromium 33.

Low Carbon Co-28Cr-6Mo Alloy (ASTM F1537 Alloy 1, ISO 5832-12 Alloy 1, R31537)Chromium Alloy 33 (R20033)

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		14 to 23
Elongation at Break, %		45

Poisson's Ratio		0.29
Poisson's Ratio		0.27

Shear Modulus, GPa		87
Shear Modulus, GPa		81

Tensile Strength: Ultimate (UTS), MPa		1000 to 1340
Tensile Strength: Ultimate (UTS), MPa		850

Tensile Strength: Yield (Proof), MPa		590 to 940
Tensile Strength: Yield (Proof), MPa		430

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		320

Specific Heat Capacity, J/kg-K		450
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Density, g/cm³		8.4
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		8.1
Embodied Carbon, kg CO₂/kg material		6.0

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		84

Embodied Water, L/kg		530
Embodied Water, L/kg		250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		140 to 200
Resilience: Ultimate (Unit Rupture Work), MJ/m³		320

Resilience: Unit (Modulus of Resilience), kJ/m³		780 to 1990
Resilience: Unit (Modulus of Resilience), kJ/m³		450

Stiffness to Weight: Axial, points		15
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		33 to 44
Strength to Weight: Axial, points		30

Strength to Weight: Bending, points		26 to 32
Strength to Weight: Bending, points		25

Thermal Shock Resistance, points		24 to 32
Thermal Shock Resistance, points		21

Alloy Composition

Carbon (C), %		0 to 0.14
Carbon (C), %		0 to 0.015

Chromium (Cr), %		26 to 30
Chromium (Cr), %		31 to 35

Cobalt (Co), %		58.9 to 69
Cobalt (Co), %		0

Copper (Cu), %		0
Copper (Cu), %		0.3 to 1.2

Iron (Fe), %		0 to 0.75
Iron (Fe), %		25.7 to 37.9

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0 to 2.0

Molybdenum (Mo), %		5.0 to 7.0
Molybdenum (Mo), %		0.5 to 2.0

Nickel (Ni), %		0 to 1.0
Nickel (Ni), %		30 to 33

Nitrogen (N), %		0 to 0.25
Nitrogen (N), %		0.35 to 0.6

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.5

Sulfur (S), %		0
Sulfur (S), %		0 to 0.010