R31537 Cobalt vs. Grade 2 Babbitt Metal
R31537 cobalt belongs to the cobalt alloys classification, while grade 2 Babbitt Metal belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is R31537 cobalt and the bottom bar is grade 2 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 53 |
| Poisson's Ratio | 0.29 | |
| 0.35 |
| Shear Modulus, GPa | 87 | |
| 19 |
| Tensile Strength: Yield (Proof), MPa | 590 to 940 | |
| 42 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 72 |
| Melting Completion (Liquidus), °C | 1360 | |
| 350 |
| Melting Onset (Solidus), °C | 1290 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 230 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 7.3 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 12 |
| Embodied Energy, MJ/kg | 110 | |
| 200 |
| Embodied Water, L/kg | 530 | |
| 1240 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 780 to 1990 | |
| 17 |
| Stiffness to Weight: Axial, points | 15 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 24 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 7.0 to 8.0 |
| Arsenic (As), % | 0 | |
| 0 to 0.1 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.14 | |
| 0 |
| Chromium (Cr), % | 26 to 30 | |
| 0 |
| Cobalt (Co), % | 58.9 to 69 | |
| 0 |
| Copper (Cu), % | 0 | |
| 3.0 to 4.0 |
| Iron (Fe), % | 0 to 0.75 | |
| 0 to 0.080 |
| Lead (Pb), % | 0 | |
| 0 to 0.35 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Tin (Sn), % | 0 | |
| 87.3 to 90 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |