Machinable Glass-ceramic vs. Low Expansion Glass-ceramic
Both machinable glass-ceramic and low expansion glass-ceramic are glass and glass-ceramics. There are 18 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is machinable glass-ceramic and the bottom bar is low expansion glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 83 |
| Flexural Strength, MPa | 96 | |
| 35 |
| Knoop Hardness | 250 | |
| 530 |
| Poisson's Ratio | 0.29 | |
| 0.22 |
| Tensile Strength: Ultimate (UTS), MPa | 84 | |
| 53 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 760 | |
| 690 |
| Specific Heat Capacity, J/kg-K | 790 | |
| 800 |
| Thermal Conductivity, W/m-K | 1.2 | |
| 1.5 |
| Thermal Expansion, µm/m-K | 21 | |
| 1.7 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.4 | |
| 5.7 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 2.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 19 |
| Stiffness to Weight: Bending, points | 51 | |
| 59 |
| Strength to Weight: Axial, points | 8.8 | |
| 6.1 |
| Strength to Weight: Bending, points | 16 | |
| 13 |
| Thermal Diffusivity, mm2/s | 0.56 | |
| 0.76 |
| Thermal Shock Resistance, points | 4.3 | |
| 28 |