Machinable Glass-ceramic vs. Optical Silicon
Machinable glass-ceramic belongs to the glass and glass-ceramics classification, while optical silicon belongs to the non-glass optical ceramics. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is machinable glass-ceramic and the bottom bar is optical silicon.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 310 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 150 |
| Flexural Strength, MPa | 96 | |
| 300 |
| Fracture Toughness, MPa-m1/2 | 2.5 | |
| 3.5 |
| Knoop Hardness | 250 | |
| 1130 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 26 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 84 | |
| 110 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 760 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 790 | |
| 700 |
| Thermal Conductivity, W/m-K | 1.2 | |
| 150 |
| Thermal Expansion, µm/m-K | 21 | |
| 3.0 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.4 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 2.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 35 |
| Stiffness to Weight: Bending, points | 51 | |
| 75 |
| Strength to Weight: Axial, points | 8.8 | |
| 13 |
| Strength to Weight: Bending, points | 16 | |
| 22 |
| Thermal Diffusivity, mm2/s | 0.56 | |
| 93 |
| Thermal Shock Resistance, points | 4.3 | |
| 18 |