Machinable Glass-ceramic vs. Potassium Chloride
Machinable glass-ceramic belongs to the glass and glass-ceramics classification, while potassium chloride belongs to the non-glass optical ceramics. There are 12 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is machinable glass-ceramic and the bottom bar is potassium chloride.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 28 |
| Poisson's Ratio | 0.29 | |
| 0.18 |
| Shear Modulus, GPa | 26 | |
| 8.5 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 790 | |
| 690 |
| Thermal Conductivity, W/m-K | 1.2 | |
| 6.5 |
| Thermal Expansion, µm/m-K | 21 | |
| 36 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.4 | |
| 4.6 |
| Electrical Dissipation At 1 MHz | 0.0050 | |
| 0.00010 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 2.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 51 | |
| 51 |
| Thermal Diffusivity, mm2/s | 0.56 | |
| 4.7 |