Magnesium Fluoride vs. Aluminum Titanate
Magnesium fluoride belongs to the non-glass optical ceramics classification, while aluminum titanate belongs to the oxide-based engineering ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is magnesium fluoride and the bottom bar is aluminum titanate.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.2 | |
| 3.2 |
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 13 |
| Stiffness to Weight: Axial, points | 22 | |
| 2.2 |
| Stiffness to Weight: Bending, points | 52 | |
| 24 |
| Thermal Conductivity, W/m-K | 28 | |
| 1.6 |
| Thermal Expansion, µm/m-K | 11 | |
| 2.9 |