Magnesium Fluoride vs. Baria-alkali-silica Glass
Magnesium fluoride belongs to the non-glass optical ceramics classification, while baria-alkali-silica glass belongs to the glass and glass-ceramics. There are 5 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is magnesium fluoride and the bottom bar is baria-alkali-silica glass.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.2 | |
| 3.0 |
| Elastic (Young's, Tensile) Modulus, GPa | 130 | |
| 80 |
| Stiffness to Weight: Axial, points | 22 | |
| 15 |
| Stiffness to Weight: Bending, points | 52 | |
| 48 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.5 |