Magnesium titanate belongs to the oxide-based engineering ceramics classification, while lead-alkali-silica glass belongs to the glass and glass-ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is magnesium titanate and the bottom bar is lead-alkali-silica glass.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 3.5
3.1
Dielectric Constant (Relative Permittivity) At 1 Hz 26
7.0
Electrical Dissipation At 1 Hz 0.0017
0.0024
Electrical Dissipation At 1 MHz 0.0013
0.0018
Electrical Resistivity Order of Magnitude, 10x Ω-m 9.0
12
Flexural Strength, MPa 80
34
Thermal Expansion, µm/m-K 8.0
9.0