Magnesium Titanate vs. Machinable Glass-ceramic
Magnesium titanate belongs to the oxide-based engineering ceramics classification, while machinable glass-ceramic belongs to the glass and glass-ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is magnesium titanate and the bottom bar is machinable glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Flexural Strength, MPa | 80 | |
| 96 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 950 | |
| 790 |
| Thermal Conductivity, W/m-K | 3.8 | |
| 1.2 |
| Thermal Expansion, µm/m-K | 8.0 | |
| 21 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 26 | |
| 6.0 |
| Dielectric Strength (Breakdown Potential), kV/mm | 9.1 | |
| 27 |
| Electrical Dissipation At 1 Hz | 0.0017 | |
| 0.0049 |
| Electrical Dissipation At 1 MHz | 0.0013 | |
| 0.0050 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 9.0 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.5 | |
| 2.7 |
Common Calculations
| Thermal Diffusivity, mm2/s | 1.1 | |
| 0.56 |