Monel K-500 vs. EN 1.4874 Stainless Steel
Monel K-500 belongs to the nickel alloys classification, while EN 1.4874 stainless steel belongs to the iron alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Monel K-500 and the bottom bar is EN 1.4874 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 210 |
| Elongation at Break, % | 25 to 36 | |
| 6.7 |
| Fatigue Strength, MPa | 260 to 560 | |
| 180 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 61 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 1100 | |
| 480 |
| Tensile Strength: Yield (Proof), MPa | 310 to 880 | |
| 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 1150 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1450 |
| Melting Onset (Solidus), °C | 1320 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 18 | |
| 13 |
| Thermal Expansion, µm/m-K | 14 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 70 |
| Density, g/cm3 | 8.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 7.6 |
| Embodied Energy, MJ/kg | 120 | |
| 110 |
| Embodied Water, L/kg | 280 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 260 | |
| 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 2420 | |
| 310 |
| Stiffness to Weight: Axial, points | 10 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 35 | |
| 16 |
| Strength to Weight: Bending, points | 19 to 27 | |
| 16 |
| Thermal Diffusivity, mm2/s | 4.8 | |
| 3.3 |
| Thermal Shock Resistance, points | 21 to 36 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 2.3 to 3.2 | |
| 0 |
| Carbon (C), % | 0 to 0.18 | |
| 0.35 to 0.65 |
| Chromium (Cr), % | 0 | |
| 19 to 22 |
| Cobalt (Co), % | 0 | |
| 18.5 to 22 |
| Copper (Cu), % | 27 to 33 | |
| 0 |
| Iron (Fe), % | 0 to 2.0 | |
| 23 to 38.9 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 3.0 |
| Nickel (Ni), % | 63 to 70.4 | |
| 18 to 22 |
| Niobium (Nb), % | 0 | |
| 0.75 to 1.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.35 to 0.85 | |
| 0 |
| Tungsten (W), % | 0 | |
| 2.0 to 3.0 |