Monel K-500 vs. Grade 366 Molybdenum
Monel K-500 belongs to the nickel alloys classification, while grade 366 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is Monel K-500 and the bottom bar is grade 366 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 300 |
| Elongation at Break, % | 25 to 36 | |
| 2.2 |
| Poisson's Ratio | 0.32 | |
| 0.3 |
| Shear Modulus, GPa | 61 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 1100 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 310 to 880 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 310 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 210 |
| Thermal Expansion, µm/m-K | 14 | |
| 7.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 12 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 27 |
| Embodied Energy, MJ/kg | 120 | |
| 340 |
| Embodied Water, L/kg | 280 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 260 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 2420 | |
| 370 |
| Stiffness to Weight: Axial, points | 10 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 18 |
| Strength to Weight: Axial, points | 21 to 35 | |
| 13 |
| Strength to Weight: Bending, points | 19 to 27 | |
| 13 |
| Thermal Shock Resistance, points | 21 to 36 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 2.3 to 3.2 | |
| 0 |
| Carbon (C), % | 0 to 0.18 | |
| 0 to 0.030 |
| Copper (Cu), % | 27 to 33 | |
| 0 |
| Iron (Fe), % | 0 to 2.0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 66.9 to 73 |
| Nickel (Ni), % | 63 to 70.4 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0.35 to 0.85 | |
| 0 |
| Tungsten (W), % | 0 | |
| 27 to 33 |