Monel R-405 vs. N07041 Nickel
Both Monel R-405 and N07041 nickel are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is Monel R-405 and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 220 |
| Elongation at Break, % | 9.1 to 39 | |
| 14 |
| Fatigue Strength, MPa | 210 to 250 | |
| 540 |
| Shear Strength, MPa | 350 to 370 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 630 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 190 to 350 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1300 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 450 |
| Thermal Conductivity, W/m-K | 23 | |
| 11 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 170 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 370 | |
| 2510 |
| Stiffness to Weight: Axial, points | 10 | |
| 15 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 20 | |
| 47 |
| Strength to Weight: Bending, points | 17 to 18 | |
| 34 |
| Thermal Diffusivity, mm2/s | 5.9 | |
| 3.0 |
| Thermal Shock Resistance, points | 17 to 20 | |
| 38 |