NEMA Laminate vs. PA 6/10
NEMA laminate belongs to the thermoset plastics classification, while PA 6/10 belongs to the thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is NEMA laminate and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.3 to 1.9 | |
| 1.1 |
| Dielectric Strength (Breakdown Potential), kV/mm | 12 to 21 | |
| 15 to 19 |
| Flexural Modulus, GPa | 6.4 to 18 | |
| 1.4 to 2.0 |
| Flexural Strength, MPa | 87 to 340 | |
| 48 to 59 |
| Impact Strength: Notched Izod, J/m | 20 to 430 | |
| 85 |
| Maximum Temperature: Mechanical, °C | 120 to 200 | |
| 80 |
| Strength to Weight: Axial, points | 8.3 to 40 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 17 to 50 | |
| 25 to 30 |
| Tensile Strength: Ultimate (UTS), MPa | 55 to 260 | |
| 45 to 60 |
| Water Absorption After 24 Hours, % | 0.17 to 3.5 | |
| 0.26 |