Nickel 601 vs. ACI-ASTM CA40 Steel
Nickel 601 belongs to the nickel alloys classification, while ACI-ASTM CA40 steel belongs to the iron alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is nickel 601 and the bottom bar is ACI-ASTM CA40 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 10 to 38 | |
| 10 |
| Fatigue Strength, MPa | 220 to 380 | |
| 460 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 890 | |
| 910 |
| Tensile Strength: Yield (Proof), MPa | 290 to 800 | |
| 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 750 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1440 |
| Melting Onset (Solidus), °C | 1360 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 25 |
| Thermal Expansion, µm/m-K | 14 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 3.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 3.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 7.5 |
| Density, g/cm3 | 8.3 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 2.0 |
| Embodied Energy, MJ/kg | 110 | |
| 28 |
| Embodied Water, L/kg | 280 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 200 | |
| 89 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 1630 | |
| 1910 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 30 | |
| 33 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 27 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 6.7 |
| Thermal Shock Resistance, points | 17 to 23 | |
| 33 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 1.7 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0.2 to 0.4 |
| Chromium (Cr), % | 21 to 25 | |
| 11.5 to 14 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 |
| Iron (Fe), % | 7.7 to 20 | |
| 81.5 to 88.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 58 to 63 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.040 |