Nickel 617 vs. AISI 310MoLN Stainless Steel

Nickel 617 belongs to the nickel alloys classification, while AISI 310MoLN stainless steel belongs to the iron alloys. They have 48% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is AISI 310MoLN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 40
28
Fatigue Strength, MPa 220
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 80
80
Shear Strength, MPa 510
400
Tensile Strength: Ultimate (UTS), MPa 740
610
Tensile Strength: Yield (Proof), MPa 280
290

Thermal Properties

Latent Heat of Fusion, J/g 330
300
Maximum Temperature: Mechanical, °C 1010
1100
Melting Completion (Liquidus), °C 1380
1420
Melting Onset (Solidus), °C 1330
1380
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 75
28
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
5.0
Embodied Energy, MJ/kg 140
70
Embodied Water, L/kg 350
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
140
Resilience: Unit (Modulus of Resilience), kJ/m3 190
200
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.5
3.7
Thermal Shock Resistance, points 21
14

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0 to 0.020
Chromium (Cr), % 20 to 24
24 to 26
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
45.2 to 53.8
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 8.0 to 10
1.6 to 2.6
Nickel (Ni), % 44.5 to 62
20.5 to 23.5
Nitrogen (N), % 0
0.090 to 0.15
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.010