Nickel 617 vs. ASTM A182 Grade F11 Class 1

Nickel 617 belongs to the nickel alloys classification, while ASTM A182 grade F11 class 1 belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is ASTM A182 grade F11 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
23
Fatigue Strength, MPa 220
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 510
300
Tensile Strength: Ultimate (UTS), MPa 740
470
Tensile Strength: Yield (Proof), MPa 280
230

Thermal Properties

Latent Heat of Fusion, J/g 330
260
Maximum Temperature: Mechanical, °C 1010
430
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 75
2.9
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.6
Embodied Energy, MJ/kg 140
21
Embodied Water, L/kg 350
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
89
Resilience: Unit (Modulus of Resilience), kJ/m3 190
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 21
14

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0.050 to 0.15
Chromium (Cr), % 20 to 24
1.0 to 1.5
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
96 to 97.7
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 8.0 to 10
0.44 to 0.65
Nickel (Ni), % 44.5 to 62
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0.5 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030