Nickel 617 belongs to the nickel alloys classification, while AWS BAg-3 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is AWS BAg-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
80
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 80
30
Tensile Strength: Ultimate (UTS), MPa 740
170

Thermal Properties

Latent Heat of Fusion, J/g 330
120
Melting Completion (Liquidus), °C 1380
690
Melting Onset (Solidus), °C 1330
630
Specific Heat Capacity, J/kg-K 450
290
Thermal Expansion, µm/m-K 12
22

Otherwise Unclassified Properties

Density, g/cm3 8.5
9.3
Embodied Carbon, kg CO2/kg material 10
49
Embodied Energy, MJ/kg 140
770

Common Calculations

Stiffness to Weight: Axial, points 14
4.8
Stiffness to Weight: Bending, points 23
15
Strength to Weight: Axial, points 24
5.1
Strength to Weight: Bending, points 21
7.3
Thermal Shock Resistance, points 21
6.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Cadmium (Cd), % 0
15 to 17
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
14.5 to 16.5
Iron (Fe), % 0 to 3.0
0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 44.5 to 62
2.5 to 3.5
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
49 to 51
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
13.5 to 17.5
Residuals, % 0
0 to 0.15