Nickel 617 vs. AWS E110C-K3

Nickel 617 belongs to the nickel alloys classification, while AWS E110C-K3 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is AWS E110C-K3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
17
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 740
870
Tensile Strength: Yield (Proof), MPa 280
760

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
48
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 75
3.4
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.7
Embodied Energy, MJ/kg 140
23
Embodied Water, L/kg 350
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
140
Resilience: Unit (Modulus of Resilience), kJ/m3 190
1550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
31
Strength to Weight: Bending, points 21
26
Thermal Diffusivity, mm2/s 3.5
13
Thermal Shock Resistance, points 21
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0 to 0.15
Chromium (Cr), % 20 to 24
0 to 0.15
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.35
Iron (Fe), % 0 to 3.0
92.6 to 98.5
Manganese (Mn), % 0 to 1.0
0.75 to 2.3
Molybdenum (Mo), % 8.0 to 10
0.25 to 0.65
Nickel (Ni), % 44.5 to 62
0.5 to 2.5
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.025
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5