Nickel 617 vs. AWS ER80S-B6

Nickel 617 belongs to the nickel alloys classification, while AWS ER80S-B6 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is AWS ER80S-B6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
19
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
74
Tensile Strength: Ultimate (UTS), MPa 740
620
Tensile Strength: Yield (Proof), MPa 280
540

Thermal Properties

Latent Heat of Fusion, J/g 330
260
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 75
4.7
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.8
Embodied Energy, MJ/kg 140
24
Embodied Water, L/kg 350
71

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 190
750
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 21
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0 to 0.1
Chromium (Cr), % 20 to 24
4.5 to 6.0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.35
Iron (Fe), % 0 to 3.0
90.6 to 94.7
Manganese (Mn), % 0 to 1.0
0.4 to 0.7
Molybdenum (Mo), % 8.0 to 10
0.45 to 0.65
Nickel (Ni), % 44.5 to 62
0 to 0.6
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.025
Residuals, % 0
0 to 0.5