Nickel 617 vs. EN 1.4612 Stainless Steel

Nickel 617 belongs to the nickel alloys classification, while EN 1.4612 stainless steel belongs to the iron alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is EN 1.4612 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
11
Fatigue Strength, MPa 220
860 to 950
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 510
1010 to 1110
Tensile Strength: Ultimate (UTS), MPa 740
1690 to 1850
Tensile Strength: Yield (Proof), MPa 280
1570 to 1730

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Maximum Temperature: Mechanical, °C 1010
790
Melting Completion (Liquidus), °C 1380
1450
Melting Onset (Solidus), °C 1330
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 75
16
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
3.6
Embodied Energy, MJ/kg 140
50
Embodied Water, L/kg 350
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
190 to 210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 24
60 to 65
Strength to Weight: Bending, points 21
40 to 43
Thermal Shock Resistance, points 21
58 to 63

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
1.4 to 1.8
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0 to 0.015
Chromium (Cr), % 20 to 24
11 to 12.5
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
71.5 to 75.5
Manganese (Mn), % 0 to 1.0
0 to 0.1
Molybdenum (Mo), % 8.0 to 10
1.8 to 2.3
Nickel (Ni), % 44.5 to 62
10.2 to 11.3
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.010
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.015
0 to 0.0050
Titanium (Ti), % 0
0.2 to 0.5