Nickel 617 vs. EN 1.4807 Stainless Steel

Nickel 617 belongs to the nickel alloys classification, while EN 1.4807 stainless steel belongs to the iron alloys. They have 56% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is EN 1.4807 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
4.5
Fatigue Strength, MPa 220
120
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 740
480
Tensile Strength: Yield (Proof), MPa 280
250

Thermal Properties

Latent Heat of Fusion, J/g 330
320
Maximum Temperature: Mechanical, °C 1010
1000
Melting Completion (Liquidus), °C 1380
1390
Melting Onset (Solidus), °C 1330
1350
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
12
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 75
39
Density, g/cm3 8.5
8.0
Embodied Carbon, kg CO2/kg material 10
6.8
Embodied Energy, MJ/kg 140
97
Embodied Water, L/kg 350
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
18
Resilience: Unit (Modulus of Resilience), kJ/m3 190
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 3.5
3.2
Thermal Shock Resistance, points 21
12

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0.3 to 0.5
Chromium (Cr), % 20 to 24
17 to 20
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
36.6 to 46.7
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 8.0 to 10
0 to 0.5
Nickel (Ni), % 44.5 to 62
34 to 36
Niobium (Nb), % 0
1.0 to 1.8
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.015
0 to 0.030