Nickel 617 vs. EN 1.5805 Steel

Nickel 617 belongs to the nickel alloys classification, while EN 1.5805 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is EN 1.5805 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 740
460 to 1180

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1010
430
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 75
3.1
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
1.6
Embodied Energy, MJ/kg 140
21
Embodied Water, L/kg 350
53

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
16 to 42
Strength to Weight: Bending, points 21
17 to 32
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 21
13 to 35

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0.070 to 0.12
Chromium (Cr), % 20 to 24
0.9 to 1.2
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
95.7 to 97.2
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 44.5 to 62
1.2 to 1.5
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025