Nickel 617 vs. EN 1.6570 Steel

Nickel 617 belongs to the nickel alloys classification, while EN 1.6570 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is EN 1.6570 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
11 to 17
Fatigue Strength, MPa 220
500 to 660
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 740
910 to 1130
Tensile Strength: Yield (Proof), MPa 280
760 to 1060

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1010
440
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 75
3.9
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
1.7
Embodied Energy, MJ/kg 140
23
Embodied Water, L/kg 350
56

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
120 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 190
1520 to 3010
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
32 to 40
Strength to Weight: Bending, points 21
27 to 31
Thermal Diffusivity, mm2/s 3.5
11
Thermal Shock Resistance, points 21
27 to 33

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0.28 to 0.35
Chromium (Cr), % 20 to 24
1.0 to 1.4
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
94 to 96.2
Manganese (Mn), % 0 to 1.0
0.6 to 1.0
Molybdenum (Mo), % 8.0 to 10
0.3 to 0.5
Nickel (Ni), % 44.5 to 62
1.6 to 2.1
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.015