Nickel 617 vs. SAE-AISI 1070 Steel

Nickel 617 belongs to the nickel alloys classification, while SAE-AISI 1070 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is SAE-AISI 1070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
10 to 13
Fatigue Strength, MPa 220
270 to 350
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
72
Shear Strength, MPa 510
380 to 460
Tensile Strength: Ultimate (UTS), MPa 740
640 to 760
Tensile Strength: Yield (Proof), MPa 280
420 to 560

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
50
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
10
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
12

Otherwise Unclassified Properties

Base Metal Price, % relative 75
1.8
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.4
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 350
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
59 to 86
Resilience: Unit (Modulus of Resilience), kJ/m3 190
470 to 850
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
23 to 27
Strength to Weight: Bending, points 21
21 to 24
Thermal Diffusivity, mm2/s 3.5
14
Thermal Shock Resistance, points 21
21 to 25

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0.65 to 0.75
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 3.0
98.3 to 98.8
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 44.5 to 62
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0 to 0.050