Nickel 617 vs. SAE-AISI M30 Steel

Nickel 617 belongs to the nickel alloys classification, while SAE-AISI M30 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is SAE-AISI M30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 740
800 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 330
270
Melting Completion (Liquidus), °C 1380
1550
Melting Onset (Solidus), °C 1330
1500
Specific Heat Capacity, J/kg-K 450
450
Thermal Conductivity, W/m-K 13
24
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 75
26
Density, g/cm3 8.5
8.2
Embodied Carbon, kg CO2/kg material 10
7.2
Embodied Energy, MJ/kg 140
100
Embodied Water, L/kg 350
120

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
27 to 74
Strength to Weight: Bending, points 21
24 to 46
Thermal Diffusivity, mm2/s 3.5
6.6
Thermal Shock Resistance, points 21
25 to 67

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
0.75 to 0.85
Chromium (Cr), % 20 to 24
3.5 to 4.3
Cobalt (Co), % 10 to 15
4.5 to 5.5
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
75.2 to 80.9
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 8.0 to 10
7.8 to 9.0
Nickel (Ni), % 44.5 to 62
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.45
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
1.3 to 2.3
Vanadium (V), % 0
1.0 to 1.4