Nickel 684 vs. EN 1.4923 Stainless Steel
Nickel 684 belongs to the nickel alloys classification, while EN 1.4923 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is nickel 684 and the bottom bar is EN 1.4923 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 | |
| 12 to 21 |
| Fatigue Strength, MPa | 390 | |
| 300 to 440 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Reduction in Area, % | 17 | |
| 40 to 46 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Shear Strength, MPa | 710 | |
| 540 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 1190 | |
| 870 to 980 |
| Tensile Strength: Yield (Proof), MPa | 800 | |
| 470 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 740 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1450 |
| Melting Onset (Solidus), °C | 1320 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 8.0 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.9 |
| Embodied Energy, MJ/kg | 140 | |
| 41 |
| Embodied Water, L/kg | 360 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1610 | |
| 570 to 1580 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 40 | |
| 31 to 35 |
| Strength to Weight: Bending, points | 30 | |
| 26 to 28 |
| Thermal Shock Resistance, points | 34 | |
| 30 to 34 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 3.3 | |
| 0 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0.18 to 0.24 |
| Chromium (Cr), % | 15 to 20 | |
| 11 to 12.5 |
| Cobalt (Co), % | 13 to 20 | |
| 0 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 |
| Iron (Fe), % | 0 to 4.0 | |
| 83.5 to 87.1 |
| Manganese (Mn), % | 0 to 0.75 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 42.7 to 64 | |
| 0.3 to 0.8 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Titanium (Ti), % | 2.5 to 3.3 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |