Nickel 686 vs. C71520 Copper-nickel
Nickel 686 belongs to the nickel alloys classification, while C71520 copper-nickel belongs to the copper alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is nickel 686 and the bottom bar is C71520 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 140 |
| Elongation at Break, % | 51 | |
| 10 to 45 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 51 |
| Shear Strength, MPa | 560 | |
| 250 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 370 to 570 |
| Tensile Strength: Yield (Proof), MPa | 350 | |
| 140 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 260 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1170 |
| Melting Onset (Solidus), °C | 1340 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 400 |
| Thermal Conductivity, W/m-K | 9.8 | |
| 32 |
| Thermal Expansion, µm/m-K | 12 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 5.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.4 | |
| 5.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 40 |
| Density, g/cm3 | 9.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 5.0 |
| Embodied Energy, MJ/kg | 170 | |
| 73 |
| Embodied Water, L/kg | 300 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 54 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
| 67 to 680 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 24 | |
| 12 to 18 |
| Strength to Weight: Bending, points | 21 | |
| 13 to 17 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 8.9 |
| Thermal Shock Resistance, points | 21 | |
| 12 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.050 |
| Chromium (Cr), % | 19 to 23 | |
| 0 |
| Copper (Cu), % | 0 | |
| 65 to 71.6 |
| Iron (Fe), % | 0 to 5.0 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.75 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 15 to 17 | |
| 0 |
| Nickel (Ni), % | 49.5 to 63 | |
| 28 to 33 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0.020 to 0.25 | |
| 0 |
| Tungsten (W), % | 3.0 to 4.4 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |