Nickel 80A vs. 50Cr-50Ni-Cb Alloy

Nickel 80A belongs to the nickel alloys classification, while 50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals. They have 68% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is nickel 80A and the bottom bar is 50Cr-50Ni-Cb alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 22
5.6
Poisson's Ratio 0.29
0.26
Shear Modulus, GPa 74
84
Tensile Strength: Ultimate (UTS), MPa 1040
620
Tensile Strength: Yield (Proof), MPa 710
390

Thermal Properties

Latent Heat of Fusion, J/g 320
350
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 55
60
Density, g/cm3 8.3
8.0
Embodied Carbon, kg CO2/kg material 9.8
9.2
Embodied Energy, MJ/kg 140
130
Embodied Water, L/kg 280
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
30
Resilience: Unit (Modulus of Resilience), kJ/m3 1300
370
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 35
21
Strength to Weight: Bending, points 27
20
Thermal Shock Resistance, points 31
14

Alloy Composition

Aluminum (Al), % 0.5 to 1.8
0 to 0.25
Carbon (C), % 0 to 0.1
0 to 0.1
Chromium (Cr), % 18 to 21
47 to 52
Iron (Fe), % 0 to 3.0
0 to 1.0
Manganese (Mn), % 0 to 1.0
0 to 0.3
Nickel (Ni), % 69.4 to 79.7
43.3 to 51.6
Niobium (Nb), % 0
1.4 to 1.7
Nitrogen (N), % 0
0 to 0.16
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 1.8 to 2.7
0 to 0.5