Nickel 890 vs. C72500 Copper-nickel
Nickel 890 belongs to the nickel alloys classification, while C72500 copper-nickel belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is nickel 890 and the bottom bar is C72500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 78 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 420 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 210 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1130 |
| Melting Onset (Solidus), °C | 1340 | |
| 1060 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Expansion, µm/m-K | 14 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 47 | |
| 35 |
| Density, g/cm3 | 8.1 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 3.6 |
| Embodied Energy, MJ/kg | 120 | |
| 55 |
| Embodied Water, L/kg | 250 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 20 | |
| 13 to 24 |
| Strength to Weight: Bending, points | 19 | |
| 14 to 21 |
| Thermal Shock Resistance, points | 15 | |
| 14 to 27 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.050 to 0.6 | |
| 0 |
| Carbon (C), % | 0.060 to 0.14 | |
| 0 |
| Chromium (Cr), % | 23.5 to 28.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 85.2 to 89.7 |
| Iron (Fe), % | 17.3 to 33.9 | |
| 0 to 0.6 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 40 to 45 | |
| 8.5 to 10.5 |
| Niobium (Nb), % | 0.2 to 1.0 | |
| 0 |
| Silicon (Si), % | 1.0 to 2.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tantalum (Ta), % | 0.1 to 0.6 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.8 to 2.8 |
| Titanium (Ti), % | 0.15 to 0.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.2 |