Nuclear Grade Hafnium vs. C85200 Brass

Nuclear grade hafnium belongs to the otherwise unclassified metals classification, while C85200 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is nuclear grade hafnium and the bottom bar is C85200 brass.

Nuclear Grade (Grade R1) Hafnium UNS C85200 Leaded Yellow Brass

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		78
Elastic (Young's, Tensile) Modulus, GPa		110

Elongation at Break, %		25
Elongation at Break, %		28

Poisson's Ratio		0.26
Poisson's Ratio		0.32

Shear Modulus, GPa		31
Shear Modulus, GPa		40

Tensile Strength: Ultimate (UTS), MPa		350
Tensile Strength: Ultimate (UTS), MPa		270

Tensile Strength: Yield (Proof), MPa		170
Tensile Strength: Yield (Proof), MPa		95

Thermal Properties

Latent Heat of Fusion, J/g		130
Latent Heat of Fusion, J/g		180

Specific Heat Capacity, J/kg-K		140
Specific Heat Capacity, J/kg-K		380

Thermal Expansion, µm/m-K		5.9
Thermal Expansion, µm/m-K		20

Otherwise Unclassified Properties

Density, g/cm³		13
Density, g/cm³		8.4

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		73
Resilience: Ultimate (Unit Rupture Work), MJ/m³		59

Resilience: Unit (Modulus of Resilience), kJ/m³		180
Resilience: Unit (Modulus of Resilience), kJ/m³		42

Stiffness to Weight: Axial, points		3.3
Stiffness to Weight: Axial, points		7.0

Stiffness to Weight: Bending, points		11
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		7.4
Strength to Weight: Axial, points		8.9

Strength to Weight: Bending, points		8.4
Strength to Weight: Bending, points		11

Thermal Shock Resistance, points		55
Thermal Shock Resistance, points		9.3

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Antimony (Sb), %		0
Antimony (Sb), %		0 to 0.2

Copper (Cu), %		0
Copper (Cu), %		70 to 74

Hafnium (Hf), %		99.8 to 100
Hafnium (Hf), %		0

Iron (Fe), %		0
Iron (Fe), %		0 to 0.6

Lead (Pb), %		0
Lead (Pb), %		1.5 to 3.8

Nickel (Ni), %		0
Nickel (Ni), %		0 to 1.0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0
Silicon (Si), %		0 to 0.050

Sulfur (S), %		0
Sulfur (S), %		0 to 0.050

Tin (Sn), %		0
Tin (Sn), %		0.7 to 2.0

Zinc (Zn), %		0
Zinc (Zn), %		20 to 27

Residuals, %		0 to 0.23
Residuals, %		0 to 0.9