PFA vs. PA 6/12
Both PFA and PA 6/12 are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is PFA and the bottom bar is PA 6/12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 300 | |
| 30 to 120 |
| Flexural Modulus, GPa | 0.7 | |
| 1.2 to 2.2 |
| Tensile Strength: Ultimate (UTS), MPa | 30 | |
| 40 to 58 |
Thermal Properties
| Melting Onset (Solidus), °C | 300 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 1590 |
| Thermal Conductivity, W/m-K | 0.25 | |
| 0.22 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 2.1 | |
| 3.9 to 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.2 | |
| 1.1 |
| Limiting Oxygen Index (LOI), % | 80 | |
| 25 |
| Water Absorption After 24 Hours, % | 0 | |
| 0.25 |
Common Calculations
| Strength to Weight: Axial, points | 3.9 | |
| 10 to 15 |
| Strength to Weight: Bending, points | 10 | |
| 25 to 31 |
| Thermal Diffusivity, mm2/s | 0.12 | |
| 0.13 |