PFA vs. PLA
Both PFA and PLA are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is PFA and the bottom bar is PLA.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 300 | |
| 6.0 |
| Flexural Modulus, GPa | 0.7 | |
| 4.0 |
| Tensile Strength: Ultimate (UTS), MPa | 30 | |
| 50 |
Thermal Properties
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 75 | |
| 65 |
| Maximum Temperature: Mechanical, °C | 260 | |
| 50 |
| Melting Onset (Solidus), °C | 300 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 1800 |
| Thermal Conductivity, W/m-K | 0.25 | |
| 0.13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.2 | |
| 1.3 |
Common Calculations
| Strength to Weight: Axial, points | 3.9 | |
| 11 |
| Strength to Weight: Bending, points | 10 | |
| 24 |
| Thermal Diffusivity, mm2/s | 0.12 | |
| 0.058 |