PA 11 vs. Thermoplastic PI
Both PA 11 and thermoplastic PI are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is PA 11 and the bottom bar is thermoplastic PI.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 | |
| 1.4 to 1.5 |
| Elastic (Young's, Tensile) Modulus, GPa | 0.4 to 1.3 | |
| 3.7 to 20 |
| Elongation at Break, % | 80 to 130 | |
| 1.8 to 7.5 |
| Limiting Oxygen Index (LOI), % | 29 | |
| 35 |
| Specific Heat Capacity, J/kg-K | 1740 | |
| 970 to 1100 |
| Stiffness to Weight: Axial, points | 0.22 to 0.71 | |
| 1.5 to 7.9 |
| Stiffness to Weight: Bending, points | 24 to 36 | |
| 37 to 64 |
| Strength to Weight: Axial, points | 6.7 to 14 | |
| 22 to 42 |
| Strength to Weight: Bending, points | 18 to 30 | |
| 36 to 57 |
| Tensile Strength: Ultimate (UTS), MPa | 25 to 51 | |
| 110 to 220 |