PA 6/10 vs. ECO Rubber
PA 6/10 belongs to the thermoplastics classification, while ECO rubber belongs to the thermoset elastomers (rubber). There are 9 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is ECO rubber.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 1.5 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.6 to 2.3 | |
| 0.0075 |
| Elongation at Break, % | 110 to 120 | |
| 440 |
| Maximum Temperature: Mechanical, °C | 80 | |
| 130 |
| Stiffness to Weight: Axial, points | 0.78 to 1.1 | |
| 0.0029 |
| Stiffness to Weight: Bending, points | 34 to 39 | |
| 4.5 |
| Strength to Weight: Axial, points | 11 to 15 | |
| 3.0 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 9.5 |
| Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
| 16 |