PA 6/10 vs. IR Rubber
PA 6/10 belongs to the thermoplastics classification, while IR rubber belongs to the thermoset elastomers (rubber). There are 10 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is IR rubber.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 1.0 |
| Elongation at Break, % | 110 to 120 | |
| 600 |
| Limiting Oxygen Index (LOI), % | 25 | |
| 19 |
| Maximum Temperature: Decomposition, °C | 440 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 1510 | |
| 1550 |
| Strength to Weight: Axial, points | 11 to 15 | |
| 5.6 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 17 |
| Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
| 19 |
| Thermal Conductivity, W/m-K | 0.23 | |
| 0.14 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 0.1 |