PA 6/12 vs. PETG
Both PA 6/12 and PETG are thermoplastics. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is PA 6/12 and the bottom bar is PETG.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.7 to 2.2 | |
| 2.2 |
| Flexural Modulus, GPa | 1.2 to 2.2 | |
| 2.1 |
| Flexural Strength, MPa | 45 to 64 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 40 to 58 | |
| 53 |
Thermal Properties
| Melting Onset (Solidus), °C | 210 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 1590 | |
| 1200 |
| Thermal Conductivity, W/m-K | 0.22 | |
| 0.29 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 3.9 to 12 | |
| 2.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 1.3 |
| Water Absorption After 24 Hours, % | 0.25 | |
| 0.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.89 to 1.2 | |
| 1.0 |
| Stiffness to Weight: Bending, points | 38 to 41 | |
| 34 |
| Strength to Weight: Axial, points | 10 to 15 | |
| 12 |
| Strength to Weight: Bending, points | 25 to 31 | |
| 25 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 0.19 |